ConDUCTIVE MATERIAL : ConDUCTIVITY : ALUMINIUM BARREL 99.6% ALUMINIUM61.8% IACS (MIN) COPPER PALM 99.95% COPPER99.7%IACSFINAL metaL STATE FULLY ANNEALED INCLUDING JOINT JOINING METHOD FRICTION WELDING, WELDING AREA MORE THAN NOMINAL ConDUCTOR AREA. FINISHNATURAL.ALUMINIUM BARRELARE CHEMICALLY TREATED TO REDUCE ConTACT RESISTANCE AND CORROSION AND ARE FILLED ELECTRICALLY ConDCTIVE CORROSION INHABITANT WITH A JOINTING COMPOUND AND CAPPED. NOTE : 1) COMBINATOINS OF BI-metaLLIC COMPRESSION JOINTS ARE DESIGNED ON THE BASIS OF CURRENT CARRYING CAPACITY OF INDIVIDUAL CABLES. 2) IN CASE ADDITIonAL COMBINATIONS ARE REQUIRED SAME MAY WILL BE PROVIDED AGAINST SPECIFIC REQUEST. 3) SHAPE SIZE AND DIMENSIONS ARE SUBJECT TO CHANGE WITHOUT NOTICE.